- General Designation: AgCu20
- Applications: slip rings, sliding contacts, switching contacts, contacts
- Product Forms: strip, wire
- Density (g/cm³): 10.13
AgCu20
Details
- Material Behaviour
- ductile
- Comment
- Susceptible to attack by sulphur
- IACS Min. (%) [100% IACS ≙ 58 S*m/mm²]
- 70
- IACS Max. (%) [100% IACS ≙ 58 S*m/mm²]
- 77
- Temperature coefficient of electric resistivity
-
From Temperature (°C)To Temperature (°C)Hard (x10-4/K)Annealed (x10-4/K)
0 100 4.3
- Young's Modulus (GPa)
- 85
- Annealed
-
Hardness (HV)Tensile strength (MPa)Yield strength (MPa)Elongation (%)
80 - 120 300 - 400 200 - 300 > 20 - Work hardened
-
Hardness (HV)Tensile Strength (MPa)Yield Strength (MPa)Elongation (%)
130 - 190 450 - 700 450 - 600 2 - 4 - Property Range
-
Hardness (HV)Tensile Strength (MPa)Yield Strength (MPa)Elongation (%)
80 - 190 300 - 700 200 - 600 2 - 20
- Melting Range
-
From Temperature (°C)To Temperature (°C)
779 820 - Linear Coefficient of Expansion³
-
From Temperature (°C)To Temperature (°C)Coefficient (x10-6/K)
20 100 19.3
Disclaimer
The information in this data sheet contains only general information on the use of our products or examples for their application. They do not release the customer from a careful inspection of the delivered product for its fitness for the customer's particular purpose of use. Any customer's special requests regarding the particular use of a product will only be authoritative if Heraeus has confirmed to the customer in writing at the time of conclusion of a corresponding contract that the product delivered is fit for the customer's intended use. Heraeus, therefore, does not guarantee the correctness and completeness of the information regarding the customer's intended use. The customer's purchase will be governed exclusively by the written order confirmation of Heraeus and the Heraeus General Terms of Sale and Delivery, which are available at www.heraeus.com/gtc. This data sheet may be subject to changes at any time.
Discuss your solution
Get in contact with experts to discuss further steps to find the optimal solution for your process.